SV 322 A/B Two compound Condensation type fast curing silicone adhesive

Short Description:

RTV SV 322 Condensation type silicone adhesive rubber is a two-component condensation type room temperature vulcanized silicone rubber. Fast curing at room temperature, Ethanol small molecule release,no corrosion of the material. Use it with two-component dispensing machine. After curing, it forms a Soft elastomer, with excellent resistance to cold and heat alternating, anti-aging and electrical insulation, good moisture resistance, shock resistance, corona resistance and anti-leakage performance. This product does not need to use other primers, can adhere to most materials such as metal, plastic, ceramics and glass, adhesion special materials. PP, PE need to be matched with a specific primer, can also be flame or plasma on the surface of the material to be adhered Treatment improves adhesion.

Send email to us

Product Detail

Product Tags

Product Description

FEATURES

1. Dealcohol type fast curing at room temperature

2. Paste, does not flow

3. Two-component volume ratio: 1:1

4. Allow large mixing error

5. Good resistance to cold and heat.

6. Good adhesion to most substrates

7. Excellent electrical insulation

8. Meet ROHS, halogen-free, REACH certification

PACKAGING

Part A	Part B
2.6L/can, 6can/carton	2.6L/can, 6can/carton
20kg/barrel, 200kg/barrel	20kg/barrel, 200kg/barrel

BASIC USES

1. Microwave ovens, induction cookers, electric kettles and other household appliances

2. Photovoltaic modules and junction boxes

3. Car lights, skylights, interior parts

4. High efficiency air filter

TYPICAL PROPERTIES

These values are not intended for use in preparing specifications

Part A
Appearance	Black sticky
Base	Polysiloxane
Density g/cm3 (GB/T13354-1992)	1.34
Extrusion rate*0.4MPa air pressure, nozzle diameter, 2mm	120 g

Part B
Appearance	white paste
Base	Polysiloxane
Density g/cm3 (GB/T13354-1992)	1.36
Extrusion rate*0.4MPaair pressure, nozzle diameter 2mm	150 g

Mix Properties
Appearance	Black or Gray paste
Volume ratio	A:B=1 : 1
Skin time, min	5～10
Initial molding time, mins	30~60
Complete hardening time, h	24